New NMC 622 Precursor (Without Li) for Battery Cathode Material

Ni+Co+Mn (%): 60.97
Ni (%): 37.36
Co (%): 12.16
Mn (%): 11.45

H₂O: ≤1
SO₄²⁻: ≤0.5

Battery Cathode Material NMC 622 Precursor (without Li)

Description:

The ternary(NMC) precursor material is nickel cobalt manganese hydroxide NixCoyMn(1-x-y)(OH)2, and the ternary composite cathode material precursor product is made of nickel salt, cobalt salt and manganese salt as raw materials. The ratio (x:y:z) can be adjusted according to actual needs.

Parameters:

Item	Test Value	Unit	Instrument/testing method
Apperance	Black power, No impurities, no lumps, consistent color	/	Visual inspection
Tab density	2.22	g/cm3	Tap Density Meter
D10	10.8	um	Laser particle size analyzer
D50	13.9	um
D90	17.9	um
Specific surface area	/	m2/g

Element content	Ni+Co+Mn (%)	Ni (%)	Co (%)	Mn (%)	H₂O	SO₄²⁻
	60.97	37.36	12.16	11.45	≤1	≤0.5
	K (%)	Na (%)	Fe (%)	Al (%)	Mo (%)	Cr (%)
	0.0000	0.0186	0.0000	0.0020	0.0000	0.0011
	Mg (%)	Pb (%)	Cu (%)	Bi (%)	Zn (%)	Ca (%)
	0.0062	0.0045	0.0000	0.0000	0.0048	0.0188